… fluxcored wires are the lowest on the market today (between 2 and 3 ml/100gr weld metal). The demands for welding consumables are getting …

… to high temperatures (most suitable temperature range is 850 - 1100 °C), high creep strength, very good resistance to isothermal and, …

… excelent mechanical properties at low temperatures.HD < 5 ml/100 … Reh ≤ 460 MPa ISO 15608: 1.2, 1.3, 2.1, 9.2  1.5637, 1.6217, …

… offers superior wear protection, retaining its hardness up to 600ºC (1000ºF) with significant resistance to oxidation. … Aircraft gas …

… structural steels with Rp0,2 > 500 MPa. Low hydrogen content HD < 3 ml/100g even after long storage. … Reh ≤ 500 MPa, ISO 15608: 1.3, 2.1, 2.3 …

… humidity before the general requirement of less than 5ml hydrogen in 100gr weld metal is exceeded. The most important steps to prevent …

… oxidation depend on cycle frequency. In no case shall a temperature of 1000°C be exceeded. This alloy can withstand relatively severe thermic … is superior to type 309 L. … ISO 15608: 8.1  Austenit ≤ 19 % Cr , TÜV 1000: Gr. 21-30,  Type: 25% Cr, 22%Ni  1.4710, 1.4713, 1.4724, 1.4726, …

… to high temperatures (most suitable temperature range is 850 - 1100 °C), high creep strength, very good resistance to isothermal and, …

… welding properties and extreme low hydrogen content below HD 3 ml/100gr weld metal. The weldmetal is suitable for longer post weld heat …